Title: LONG-TERM PERFORMANCE OF HDPE GEOMEMBRANES AS LANDFILL LINERS
Authors: ISLAM, MOHAMMAD

Files in This Item:

File Description SizeFormat
Islam_Mohammad_Z_200901_PhD.pdf7.83 MBAdobe PDFView/Open
Keywords: Antioxidant
Degradation
Diffusive migration
Geomembrane
HDPE
Landfill
Leachate
Long-term performance
Service life
Simulated landfill liner
Temperature
Thickness
Volatile organic compounds
Geoenvironmental engineering
Geotechnical engineering
Civil engineering
Issue Date: 2009
Series/Report no.: Canadian theses
Abstract: High density polyethylene (HDPE) geomembranes are normally used as part of a composite liner for waste containment facilities such as municipal solid waste (MSW) landfills and heap leach pads. Field conditions, which include physical stresses on the geomembrane, elevated operating temperatures, and contact with leachate constituents, have the potential to affect the service life of the HDPE geomembranes. This thesis examined the long-term performance of different HDPE geomembranes based on both conventional laboratory accelerated immersion tests and simulated landfill liner tests. A 1.5mm HDPE geomembrane was immersed in different synthetic leachates at different temperatures in order to evaluate the effects of leachate chemical constituents on the depletion of antioxidants. The results showed that a basic leachate with trace metals, surfactant, and a reducing agent was the most appropriate for evaluating the potential degradation of HDPE geomembranes. A similar immersion test was performed to evaluate the effects of thickness on the ageing of HDPE geomembranes. Three commercially available HDPE geomembranes having nominal thicknesses of 1.5, 2.0, and 2.5mm were immersed in a synthetic leachate at four different temperatures in this experiment. The results showed that a thicker geomembrane may have a longer service life if other things are similar. The depletion of antioxidants from a 1.5mm thick HDPE geomembrane was examined by conducting accelerated ageing tests at 55, 70, and 85oC under simulated landfill liner conditions. The results showed that the antioxidant depletion rate was consistently lower for the simulated landfill liner tests compared to the leachate immersion tests. The effectiveness of the aged HDPE geomembrane on the migration of volatile organic compounds (VOCs) was examined by conducting diffusion and partitioning tests using both unaged and aged HDPE geomembranes. The results showed that the ageing of HDPE geomembranes did not increase diffusive migration of organic contaminants, provided that the geomembrane remained intact. A new method was developed to estimate the service life of the HDPE geomembrane based on the landfill liner temperature history. The service lives of the HDPE geomembranes were calculated to be between 20 and 4700 years, depending on the geomembrane type, exposure conditions, and the time-temperature history examined.
Description: Thesis (Ph.D, Civil Engineering) -- Queen's University, 2009-01-30 09:30:49.135
URI: http://hdl.handle.net/1974/1686
Appears in Collections:Civil Engineering Graduate Theses
Queen's Theses & Dissertations

Items in QSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

  DSpace Software Copyright © 2002-2008  The DSpace Foundation - TOP