Title: Lattice Strain and Texture of Plastically Deformed Zircaloy-2 at 77K
Authors: Judge, COLIN

Files in This Item:

File Description SizeFormat
Judge_Colin_D_200909_MSc.pdf6.73 MBAdobe PDFView/Open
Keywords: Zirconium
slip
twinning
deformation
lattice strain
EBSD
texture
Zircaloy-2
Issue Date: 2009
Series/Report no.: Canadian theses
Abstract: Zircaloy-2 is used extensively in the nuclear industry as a structural material for the reactor core in both light and heavy water reactors. The intergranular strains and texture greatly affect the mechanical properties of the material while in operation. Understanding the plastic deformation of Zircaloy-2 will improve on current plastic deformation models, particularly for twinning mechanisms, which are more active at lower temperatures, and are not yet well understood. For this study, neutron diffraction was used to track the lattice spacing and peak intensity in warm-rolled and recrystallized Zircaloy-2 slab for various crystallographic orientations at 77 K. Tests were performed in all three principle directions under tension and compression. The texture was measured for the deformed samples to help interpret the dominant deformation systems and then Electron Back Scattering Diffraction was used to identify and image the active twinning modes. Prism <a> slip, basal <a> slip, {10-12} and {11-2 1} tensile twinning, and {11-2 2} compression twinning were found to be contributing deformation systems in Zircaloy-2 at 77K. In this study, the diffraction elastic constants for Zircaloy-2 at room temperature and 77K are reported for the first time in open literature. These values will be useful in future experimental work by allowing a conversion between lattice spacing and residual stress.
Description: Thesis (Master, Mechanical and Materials Engineering) -- Queen's University, 2009-09-24 13:41:25.371
URI: http://hdl.handle.net/1974/5345
Appears in Collections:Mechanical and Materials Engineering Graduate Theses
Queen's Theses & Dissertations

Items in QSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

  DSpace Software Copyright © 2002-2008  The DSpace Foundation - TOP