EFFECTS OF TWO WARM-MIX ADDITIVES ON AGING, RHEOLOGICAL AND FAILURE PROPERTIES OF ASPHALT CEMENTS
MetadataShow full item record
Sustainable road construction and maintenance could be supported when excellent warm-mix additives are employed in the modification of asphalt. These warm-mix additives provide remedies for today’s requirements such as fatigue cracking resistance, durability, thermal cracking resistance, rutting resistance and resistance to moisture damage. Warm-mix additives are based on waxes and surfactants which reduce energy consumption and carbon dioxide emissions significantly during the construction phase of the pavement. In this study, the effects of two warm mix additives, siloxane and oxidised polyethylene wax, on roofing asphalt flux (RAF) and asphalt modified with waste engine oil (655-7) were investigated to evaluate the rheological, aging and failure properties of the asphalt binders. In terms of the properties of these two different asphalts, RAF has proved to be superior quality asphalt whereas 655-7 is poor quality asphalt. The properties of the modified asphalt samples were measured by Superpave™ tests such as Dynamic Shear Rheometer (DSR) test and Bending Beam Rheometer (BBR) test as well as modified protocols such as the extended BBR (eBBR) test (LS-308) and the Double-Edge-Notched Tension (DENT) test (LS-299) after laboratory aging. In addition, the Avrami theory was used to gain an insight on the crystallization of asphalt or the waxes within the asphalt binder. This study has however shown that the eBBR and DENT tests are better tools for providing accurate specification tests to curb thermal and fatigue cracking in contemporary asphalt pavements.