Modification of a High-Temperature Electrochemical Testing Station and Experimental Development for Solid Oxide Electrolysis Cell Anode Analysis
Loading...
Authors
Clancy, Graeme
Date
2016-01-27
Type
thesis
Language
eng
Keyword
Porous Materials , Electrochemistry , Solid Oxide Electrolysis Cell Anodes , Hydrogen
Alternative Title
Abstract
A method to fabricate solid oxide electrolysis cell (SOEC) anodes in a controlled process has been developed. Adjustment of deposition rate was found to alter the anode porosity and particle size distribution. A solid oxide fuel cell (SOFC) testing system was enhanced to complete steam electrolysis testing of the cells with prepared anodes.
To prepare anodes of desirable morphology and uniform thickness the effect of spraying parameters on anode morphology were studied. Sonication of the anode inks was found to reduce particle agglomerations in the ink dispersion. A technique for obtaining and analyzing SEM cross sections of SOECs was developed to study prepared anodes. Investigation of sprayed anodes revealed that the porosity decreased as the deposition rate was increased. Using ImageJ analysis software particle size distributions of prepared anodes were determined. Anodes deposited at higher deposition rates were seen to have larger particle sizes. A greater anode deposition rate increased the likelihood of particle settling and agglomeration, leading to the decreased porosity and increased particle size in the anodes.
A membrane humidifier was developed and tested to steadily supply steam to the electrolysis cell, the first such humidifier combined with a ProbotStatTM testing rig. Using the modified testing system, a testing method for SOEC analysis was developed. The process for producing polarization curves was studied to determine the desired testing conditions. During testing hysteresis between increasing and decreasing polarization curves, and anode conditioning during constant current electrolysis were seen for some cells. The appearance or absence of both phenomena were seen to be connected.
Description
Thesis (Master, Chemical Engineering) -- Queen's University, 2016-01-25 17:34:09.465
Citation
Publisher
License
Queen's University's Thesis/Dissertation Non-Exclusive License for Deposit to QSpace and Library and Archives Canada
ProQuest PhD and Master's Theses International Dissemination Agreement
Intellectual Property Guidelines at Queen's University
Copying and Preserving Your Thesis
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.
ProQuest PhD and Master's Theses International Dissemination Agreement
Intellectual Property Guidelines at Queen's University
Copying and Preserving Your Thesis
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.