Lattice Strain Response of Zr-2 During Biaxial Deformation

dc.contributor.authorCampbell, Daleen
dc.contributor.departmentMechanical and Materials Engineeringen
dc.contributor.supervisorDaymond, Mark R.en
dc.date2014-01-13 11:24:21.692's University at Kingstonen
dc.descriptionThesis (Master, Mechanical and Materials Engineering) -- Queen's University, 2014-01-13 11:24:21.692en
dc.description.abstractPseudo-plane strain compression tests are carried out on rolled plate Zircaloy-2 using different combinations of loaded and constrained sample directions relative to the plate principal directions. Lattice strains are measured for 17 out of 18 possible measureable sample directions. The inability to obtain true plane strain led to little effect of the compression rig on deformation during elastic loading; however noticeable differences are seen when compared to similar uniaxial data for Zircaloy-2 in the plastic region. Work hardening increased with increased constraint and was affected by the configuration of loaded and constrained sample directions. Constraint showed significant effects on twinning when twinning was present. For the RD loaded cases the initiation of twinning occurs at -318 MPa for the RD/ND case (RD loaded, ND constrained direction) and -420 MPa for the RD/TD case. Intensity profiles of the (0002) and {101 ̅ 0} indicate that more twinning occurs in the RD/TD case than the RD/ND case. For TD/YD an amplification of twinning was seen in the TD/RD when compared to the TD/ND. This is indicated both by texture results as well as the intensity profiles of the (0002) and {101 ̅ 0}. Using the experimental data an elastic-plastic self-consistent (EPSC) code was used to probe the micromechanical processes that are occurring when the compression rig is operated. The experimental data was used further to constrain the hardening parameters of the EPSC code using an inverse approach. The EPSC code was able to capture the relative activity of the twinning characteristics found by the experimental data but unable to truly capture the evolution of the (0002) lattice strains when twinning occurs.en
dc.relation.ispartofseriesCanadian thesesen
dc.rightsThis publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.en
dc.subjectBiaxial Deformationen
dc.subjectNeutron Diffractionen
dc.titleLattice Strain Response of Zr-2 During Biaxial Deformationen
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
6.11 MB
Adobe Portable Document Format
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
1.64 KB
Item-specific license agreed upon to submission