Radiation Damage Effect on Mechanical Properties and Microstructure of X-750 Ni-based Superalloy
Loading...
Authors
Changizian, Pooyan
Date
Type
thesis
Language
eng
Keyword
Radiatio Damage , X-750 superalloy , Nano-scale mechanical test , Transmission Electron Microscopy , Defects , Gamma-prime Precipitate , Obstacle Hardening Model
Alternative Title
Abstract
Inconel X-750 is an age-hardened Ni-based superalloy with high mechanical strength and creep resistance. The X-750 alloy is extensively used in the cores of reactors, such as spacers in CANada Deuterium Uranium (CANDU) fuel channels. The recent mechanical tests on the ex-service Inconel X-750 spacers indicate significant embrittlement and reduced load carrying capacity compared to as installed condition. The primary degradation mechanism remains unclear, and thus provides the focus of this investigation. Heavy-ion irradiation was employed as an emulator for neutron irradiation to explore the microstructural evolution and mechanical property degradation in X-750 Ni-based superalloy. The ion-irradiation has been conducted at different temperatures and up to different doses. In addition, helium-implantation prior to heavy-ion irradiation was used to investigate the effect of helium on microstructural changes. The discussion of the microstructural evolution is focused on characterization of irradiation-induced defects, including dislocation loops and cavities along with examination of the stability of strengthening phase γ'-precipitates. A major contribution of this work is to utilize a focused ion beam (FIB) and transmission electron microscopy (TEM) to perform precise defect characterization. The microstructure is correlated to the mechanical properties obtained via nano-hardness test on irradiated materials. In order to estimate the individual contribution of defects in radiation-induced hardening, three different obstacle-hardening models have been applied to fit TEM-obtained microstructural data. The superposition of contributions is made in each model and compared with nano-scale experimental results. This approach is unique to the literature since it demonstrates both the individual and the combined effects of the microstructural features on mechanical behavior. Furthermore, the effect of gamma-prime instability on mechanical properties of irradiated X-750 was investigated and the strength softening raised from disordering and also dissolution of gamma-prime was evaluated.
Description
Citation
Publisher
License
Queen's University's Thesis/Dissertation Non-Exclusive License for Deposit to QSpace and Library and Archives Canada
ProQuest PhD and Master's Theses International Dissemination Agreement
Intellectual Property Guidelines at Queen's University
Copying and Preserving Your Thesis
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.
ProQuest PhD and Master's Theses International Dissemination Agreement
Intellectual Property Guidelines at Queen's University
Copying and Preserving Your Thesis
This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.