dc.descriptionThesis (Ph.D, Mechanical and Materials Engineering) -- Queen's University, 2007-12-21 11:56:23.743en
dc.description.abstractZircaloy-2 and its sister alloy, Zircaloy-4, have extensive applications in the nuclear industry as core components in heavy water reactors and fuel cladding in both heavy and light water reactors. Intergranular stresses and texture can greatly affect the mechanical performance of these components. A complete understanding of the development of intergranular constraints and texture in Zircaloy-2 will allow an improved understanding of the plastic deformation of zirconium alloys, and the prediction of in-reactor deformation of tubes made by different manufacturing routes. Neutron diffraction was used to track the development of lattice strain and peak intensity in three dimensions for various crystallographic planes in samples cut from a rolled Zircaloy-2 slab. The samples were subject to room temperature compression or tension in-situ in the neutron spectrometer in each of the three principal directions of the slab. Textures in the deformed samples were measured using neutron diffraction. Strong evidence was found for tensile twinning in tensile tests in the plate normal direction and compression tests in the transverse and rolling directions. The lattice strain development inside the newly formed twins was recorded for the first time in a Zr alloy. An elasto-plastic self-consistent model and a visco-plastic self-consistent model were used to interpret the lattice strain and texture data, respectively. Various slip and twinning modes were considered in both models. Prism <a> slip, basal <a> slip, pyramidal <c+a> slip and tensile twinning were concluded to be indispensable, while pyramidal <a> slip was unnecessary in the modeling. The critical resolved shear stresses and hardening parameters were obtained by simultaneously achieving a ‘best-fit’ with the complete experimental data set. The effects of anisotropic latent hardening due to dislocation interactions were found to be critical, and the inclusion of Lankford coefficients as modeling constraints was necessary. This research provided a comprehensive experimental data set obtained by neutron diffraction, forming a sound basis to investigate active plastic deformation mechanisms and to rigorously test plasticity models and twinning models. The research also made a substantial improvement in understanding the plastic deformation of Zircaloy-2 through polycrystalline modeling by introducing extensive data sets to constrain the modeling parameters.en
dc.description.sponsorshipNSERC, COG, OPG and Nu-Tech Precision Metalsen
dc.format.extent6571616 bytes
dc.format.mimetypeapplication/pdf
dc.languageenen
dc.language.isoenen
dc.relation.ispartofseriesCanadian thesesen
dc.rightsThis publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner.en
dc.subjectNeutron Diffractionen
dc.subjectPolycrystalline Modelingen
dc.subjectPlastic Deformationen
dc.subjectZircaloy-2en
dc.titleLATTICE STRAIN AND TEXTURE EVOLUTION DURING ROOM-TEMPERATURE DEFORMATION IN ZIRCALOY-2en
dc.description.degreePh.Den
dc.contributor.supervisorHolt, Richard A.en
dc.contributor.supervisorDaymond, Mark R.en
dc.contributor.departmentMechanical and Materials Engineeringen


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record